20cr厚壁無縫鋼管
具有中空截(jie)(jie)面,大量用(yong)(yong)(yong)作輸(shu)送流體(ti)的管(guan)(guan)道(dao),如(ru)輸(shu)送石油(you)、天然氣、煤氣、水及(ji)某些固體(ti)物料(liao)(liao)等。與圓(yuan)鋼(gang)(gang)等實心鋼(gang)(gang)材相比,在抗彎抗扭強度(du)相同時(shi),重(zhong)量較輕,20Cr無縫(feng)鋼(gang)(gang)管(guan)(guan)是一種經濟截(jie)(jie)面鋼(gang)(gang)材,廣泛(fan)用(yong)(yong)(yong)于制(zhi)造(zao)(zao)結構件(jian)(jian)和機械(xie)零(ling)件(jian)(jian),如(ru)石油(you)鉆桿(gan)、汽(qi)車(che)傳動軸、自行車(che)架(jia)以及(ji)建筑施工(gong)中用(yong)(yong)(yong)的鋼(gang)(gang)腳手(shou)架(jia)等。用(yong)(yong)(yong)20Cr鋼(gang)(gang)管(guan)(guan)制(zhi)造(zao)(zao)環(huan)形零(ling)件(jian)(jian),可(ke)(ke)提(ti)高材料(liao)(liao)利(li)用(yong)(yong)(yong)率,簡化制(zhi)造(zao)(zao)工(gong)序(xu),節約(yue)材料(liao)(liao)和加工(gong)工(gong)時(shi),如(ru)滾動軸承(cheng)套(tao)圈、千斤頂套(tao)等,目前(qian)已廣泛(fan)用(yong)(yong)(yong)鋼(gang)(gang)管(guan)(guan)來制(zhi)造(zao)(zao)。20Cr無縫(feng)鋼(gang)(gang)管(guan)(guan)還是各(ge)種常規武器不可(ke)(ke)缺少的材料(liao)(liao),槍管(guan)(guan)、炮筒等都要(yao)鋼(gang)(gang)管(guan)(guan)來制(zhi)造(zao)(zao)。20Cr鋼(gang)(gang)管(guan)(guan)按橫截(jie)(jie)面積形狀(zhuang)的不同可(ke)(ke)分為圓(yuan)管(guan)(guan)和異型管(guan)(guan)。由于在周長相等的條件(jian)(jian)下(xia),圓(yuan)面積最大,用(yong)(yong)(yong)圓(yuan)形管(guan)(guan)可(ke)(ke)以輸(shu)送更多的流體(ti)。此外,圓(yuan)環(huan)截(jie)(jie)面在承(cheng)受內部或外部徑向壓(ya)力(li)時(shi),受力(li)較均勻,因此,絕(jue)大多數鋼(gang)(gang)管(guan)(guan)是圓(yuan)形管(guan)(guan)材。
20Cr無縫(feng)鋼管
化學成(cheng)份(%):硅:0.17~0.37
力學性能:抗拉強度 σb (MPa):≥835屈服強度 σs (MPa):≥540伸長率 δ5 (%):≥10斷面收縮(suo)率 ψ (%):≥40,沖(chong)擊吸收功Ak(J)≥47硬度:退(tui)火(huo)或高(gao)溫回火(huo)供應狀態(tai)硬度≤156HB,試樣尺寸:試樣尺寸15mm
熱處(chu)理規(gui)范及金(jin)相組(zu)織:
熱處理規范:淬火溫度(℃)第一次880,第二(er)次780~820,冷(leng)卻劑(ji)水(shui)和油。回火溫度(℃)200,冷(leng)卻劑(ji)水(shui)、空。
焊接性能:
2、厚度(du)大于(yu)15mm的20Cr零件在(zai)焊前需預熱(re)到100~150℃,若要求(qiu)不高焊前可不預熱(re),焊后也(ye)可不進行回火熱(re)處理。
|